دراسة توازنات الأطوار في الجملة الثنائية لثنائي أكسيد المنغنيز وميتا فانادات الصوديوم NaVO3 ─MnO2

الموضوعات

علوم بحتة وطبيعية

روابط وملفات

التعريف والنوع

رقم الوثيقة

fba2b234-fb96-429b-9bd4-23c3ad5cd432

رقم العقد

0

نوع الوسائط

Crawler

نوع المحتوى

الرسائل العلمية

صيغة المصدر

رسائل ماجيستير

نوع الملف

pdf text

أسماء الملفات

1960226_1.pdf

بيانات النشر

ترجمة العنوان

Thesis Submitted for getting a master's degree in chemistry competence inorganic chemistry

ألقاب المؤلفين

[{"name_ar":"رشا حسام صالح","title_ar":"اعداد","title_en":"Preparation"},{"name_ar":"محمـد ديب","title_ar":"اشراف","title_en":"Supervision"}]

اللغة

Arabic

المصدر والدورية

اسم المصدر

دراسة توازنات الأطوار في الجملة الثنائية لثنائي أكسيد المنغنيز وميتا فانادات الصوديوم NaVO3 ─MnO2

المحتوى والصفحات

عدد الصفحات

0

ترجمة الملخص

The importance of diagram system MnO2─NaVO3is in obtaining crystal phases (chemical compounds or solid solutions), Acknowledging the fact that these compounds have grade properties in the field of technology, it was im-portant to study the possibility of obtaining new phases with different mole ra-tios, and to draw phase diagram for it, especially the used compounds in this study have different crystal structures. The samples were made beginning from powders of reagent grade (MnO2and NaVO3)in (5 gr) for each of them at following percentage mole ratios of MnO2: (10, 20, 25, 30, 33.33, 50, 66.66, 70, 71, 75, 80, 90). The mixing and grinding process was made for these samples. Then, it made pills ellipsoidal using manu-ally hydraulic press, and it burned into oven at different degrees. The study was made using powder X─Rays diffraction (P─XRD), different ialthermal and thermal gravimetric analysis (TG─DTA), and infrared spectroscopy (FT─IR). The results are compared with X─Rays spectrums of grade compounds and pa-rameters of it. Then, the degrees of the formation phase changes were deter-mined. New crystal compound was formed at ratio (MnO2)10(NaVO3)90mole %, and crystal solid solution basic on it was formed to ratio (MnO2)25(NaVO3)75mole%. As well as two phases in balance( amorphousp hase+ new crystal com-pound) were formed to mole ratio (MnO2)75(NaVO3)25mole %, and amorphous solid solution was formed beginning from mole ratio (MnO2)80(NaVO3)20mole%, then the phase diagram for the studied system was drawn

كلمات الباحثين

Infrared spectroscopy FT─IR, manganese dioxide, odium metavanadate, Phase equilibrium, TG─DTA, X─Rays diffraction, التفاضلي والوزني, الجهاز الحراري, ثنائي أكسيد المنغنيز, حيود الأشعة السينية, طيف الأشعة تحت الحمراء, مخطط توازن الاطوار, ميتا فانادات الصوديوم