Tribo-Mechanical, Biocompatibility, and Corrosion Properties Investigation of Zirconium and SST 304 by Application of Hydroxyapatite/Reduced Graphene Oxide/Palladium-Platinium Nanocomposite Coatings

الموضوعات

علوم تطبيقية وتكنولوجية

الملخص

This thesis describes the synthesis of HA/rGO/Pd and HA/rGO/Pt nanocomposite thin film coatings on stainless steel 304 and pure zirconium applied via an electrodeposition method. The corrosion and biocompatibility characteristics of HA/rGO/Pd and HA/rGO/Pt nanocomposite thin films are investigated here. Biocompatibility tests were carried out on uncoated, HA-coated, HA/rGO-coated, HA/rGO/Pd-coated, and HA/rGO/Pt-coated substrates using the human cell line MDA-MB-231, which had a green fluorescent protein to report the presence of living cells. Experiments revealed that the biocompatibility of the SST 304 surface showed the best cell spreading and proliferation when coated with the HA/rGO/Pd nanocomposite. The zirconium substrate coated with HA/rGO/Pt showed decreased cell proliferation and adhesion compared with HA/rGO, showing that Pt did not improve the biocompatibility.A synthetic medium was used to conduct corrosion tests, which confirmed that the HA/rGO/Pd-coated SST 304 had a significantly higher corrosion resistance than the uncoated, HA-coated, and HA/rGO-coated SST 304 samples. In addition, the HA/rGO/Pd-coated SST 304 and the HA/rGO/Pt-coated zirconium substrates were annealed at different temperatures (200, 300, 400, and 600 oC) to investigate their corrosion and wear behaviors.The HA/rGO/Pd-coated substrate annealed at 600 °C showed better wear resistance compared with the other samples. The wear tests result of bare and electrodeposited specimens before and after heat treatment for the HA/rGO/Pt showed that the coated samples heated at 300 °C had superior resistance against wear compared with bare and electrodeposited substrates at other annealing temperatures.

روابط وملفات

التعريف والنوع

رقم الوثيقة

faeeda0f-2ad6-430a-9c15-5510a5de99fa

رقم العقد

0

نوع الوسائط

Crawler

نوع المحتوى

الرسائل العلمية

صيغة المصدر

رسائل دكتوراة

نوع الملف

pdf text

أسماء الملفات

2018134_1.pdf

بيانات النشر

ألقاب المؤلفين

[{"name_ar":"عبدالمجيد حمودة","title_ar":"اشراف","title_en":"Supervision"},{"name_ar":"هدى فضول","title_ar":"اعداد","title_en":"Preparation"}]

اللغة

English

المصدر والدورية

اسم المصدر

Tribo-Mechanical, Biocompatibility, and Corrosion Properties Investigation of Zirconium and SST 304 by Application of Hydroxyapatite/Reduced Graphene Oxide/Palladium-Platinium Nanocomposite Coatings

المحتوى والصفحات

عدد الصفحات

0

إشراف وإعداد

الإشراف

عبدالمجيد حمودة

الإعداد

هدى فضول

الاقتباسات الببليوغرافية