Élaboration et caractérisation des composites de Al-15%Zn/x%Al2O3 avec x=0, 3, 5, 7 et 10 % (Massique) par la Technique Stir Casting

الموضوعات

علوم بحتة وطبيعية

الملخص

A composite, material with a metallic basis, of alloy (Al-15%. (Wt) Zn), is prepared by using stir casting technique, reinforced with (Al2O3) particles at various percentages (0 ،3 ،5 ،7 ،and 10 Wt. %).The result of test have shown an improvement in the value of hardness, the increasing in weight percentage of the reinforcement material (Al2O3) lead to increase the hardness, compared to the base alloy. The particles (Al2O3) are distributed in the base alloy. Where the aluminum oxide, act as obstacle which restricts the movement of the dislocation, which leads to increased hardness of the composite material.X-ray diffraction schemes were also shown special peaks of the α-Al aluminum phase and hexagonal Zn phase.Key words: Composite material, (Al-05%. (Wt) Zn), (Technique Stir Casting), Alumina oxide (Al2O3), hardness Hv, x-ray.

روابط وملفات

التعريف والنوع

رقم الوثيقة

fa92ee9a-7cff-46ce-b852-46662eebdd01

رقم العقد

0

نوع الوسائط

Crawler

نوع المحتوى

الرسائل العلمية

صيغة المصدر

ماستر (LMD)

نوع الملف

pdf text

أسماء الملفات

2073239_1.pdf

بيانات النشر

ألقاب المؤلفين

[{"name_ar":"Djamel Abdelkebir","title_ar":"اشراف","title_en":"Supervision"},{"name_ar":"Khawla Ben Geusmia ","title_ar":"اعداد","title_en":"Preparation"},{"name_ar":"Miloud Ibrir","title_ar":"اشراف","title_en":"Supervision"}]

اللغة

French

المصدر والدورية

اسم المصدر

Élaboration et caractérisation des composites de Al-15%Zn/x%Al2O3 avec x=0, 3, 5, 7 et 10 % (Massique) par la Technique Stir Casting

المحتوى والصفحات

عدد الصفحات

0

إشراف وإعداد

الإشراف

Djamel Abdelkebir, Miloud Ibrir

الإعداد

Khawla Ben Geusmia

الاقتباسات الببليوغرافية