Effect of Acetylene Rates and Temperature Variations of Iron and Cobalt Nanoparticles in Carbon Nanotubes Fabrication

الموضوعات

علوم بحتة وطبيعية

الملخص

In this research, low pressure chemical vapor deposition system(LPCVD) was used to produced carbon nanotubes. It has been used for sixteen samples of iron Fe and cobalt Co according to actylene C2H2 rates change of (10, 20, 30, and 40sccm) and with temperature rates varied of (450ºC, 650ºC, 850ºC, and 950ºC) respectively. The morphology was studied by using scanning electron microscope (SEM).It has been found carbon nanotubes CNTs was produced when acetylene rates was 20sccm at 950ºC for iron and 650ºC for cobalt. Also; it was found that the diameter of the tubes were 2~3 nm by using scanning electron microscope for both Fe and Co. The result obtained was compared with fractal analysis where the diameter ranges from 1.62 nm to 1.8 nm for both Fe and Co. This conformity between the ranges confirms the reality of the results.

روابط وملفات

التعريف والنوع

رقم الوثيقة

f9ec1c3f-9351-4a46-bb21-c4d70f5cd2c8

رقم العقد

0

نوع الوسائط

Crawler

نوع المحتوى

الرسائل العلمية

صيغة المصدر

رسائل دكتوراة

نوع الملف

pdf text

أسماء الملفات

19329_1.pdf, 19329_2.pdf, 19329_3.pdf, 19329_4.pdf, 19329_5.pdf, 19329_6.pdf, 19329_7.pdf, 19329_8.pdf

بيانات النشر

ترجمة العنوان

مشكلة - يوجد بحثين يحتاجوا للاضافة في تسجيلات اخرى

ألقاب المؤلفين

[{"name_ar":"Hassan Idriss Abaker Idriss","title_ar":"اعداد","title_en":"Preparation"},{"name_ar":"Mubarak Dirar Abdalla","title_ar":"اشراف","title_en":"Supervision"}]

اللغة

English

المصدر والدورية

اسم المصدر

Effect of Acetylene Rates and Temperature Variations of Iron and Cobalt Nanoparticles in Carbon Nanotubes Fabrication

المحتوى والصفحات

عدد الصفحات

0

ترجمة الملخص

تأثير معدلات الأستالين وتغيرات درجة الحرارة للحديد والكوبالت في صنع أنابيب الكربون النانوية

إشراف وإعداد

الإشراف

Mubarak Dirar Abdalla

الإعداد

Hassan Idriss Abaker Idriss

الاقتباسات الببليوغرافية