Improving the Economic Viability and Flexural Strength Performance of Dowel Laminated Casaurina Glauca Patch-wood

الموضوعات

علوم تطبيقية وتكنولوجية

الملخص

The purpose of this study was to determine the strength of local casuarina glauca patchwood under artificial weathering presenting the changes of strength of wood along fibers. The study involved wood of similar density - half factorial design experiment was used with four factors to use fewer samples to have a total of 8. The specimens were exposed to artificial weathering consisting of soaking wood in water, drying at 60 °C, and exposure to UV radiation. Three-step aging cycle was repeated 8 times. In general, the tested wood species changed their compressive strength differently under the influence of artificial weathering. The process of artificial weathering caused a loss of strength of all tested wood species. The extent of changes depended on initial properties of wood (especially density) and anatomy. Two experiments were implemented; one with vertical patch-wood alignments and the other with horizontal patch-wood alignments. Since this research was conducted to determine the strength of block boards made from local casuarina glauca wood, the strength was determined in the longitudinal direction. it is conducted that the strength of block boards can carry a normal stress of (185.75 N/mm2) with 3 points bending test and in the vertical alignment. whilst with 4 points bending test, it can carry a normal stress of (158.55 N/mm2). The weakest can carry a normal stress of (60.31 N/mm2) while on 4 points bending test it can carry a normal stress of (52.60 n/mm2). It was determined that the presence of intermediate biscuit did not help in the strength but it weakens the wood but helps only after the cycling variable. Also, it was determined that PVAc is better the M.U.F. However, the horizontal alignment experiment recorded a shear force result of (3.54 N/mm2) in the 3 points-test and (2.5 N/m2) in the 4 points test while the weakest can carry a force of 0.94 for both tests.

روابط وملفات

التعريف والنوع

رقم الوثيقة

07d4e7e5-0a58-48a7-8074-6d6800c46449

رقم العقد

0

نوع الوسائط

Crawler

نوع المحتوى

الرسائل العلمية

صيغة المصدر

رسائل ماجيستير

نوع الملف

pdf text

أسماء الملفات

845650_3.pdf

بيانات النشر

ألقاب المؤلفين

[{"name_ar":"Hesham El Seginy","title_ar":"اعداد","title_en":"Preparation"},{"name_ar":"Khaled nassar","title_ar":"اشراف","title_en":"Supervision"}]

اللغة

English

المصدر والدورية

اسم المصدر

Improving the Economic Viability and Flexural Strength Performance of Dowel Laminated Casaurina Glauca Patch-wood

المحتوى والصفحات

عدد الصفحات

0

إشراف وإعداد

الإشراف

Khaled nassar

الإعداد

Hesham El Seginy

الاقتباسات الببليوغرافية